| 秦沈客运专线钢轨铝热焊缺陷分析(43 卷) |
| 英文标题 |
| * |
| 摘要 |
| 与既有线相比，在秦沈客运专线建设中使用铝热焊具有如下特点：用量集中、施工时间及范 围跨度大、操作人员熟练程度不均。因此，进行现场铝热焊施工时，由于焊接材料及操作因 素的影响，出现一些焊接缺陷。文章分析了这些缺陷产生的原因并提出解决措施。 |
| 作者 |
| 新闻作者:胡智博，李 力，邹立顺，裘德海 |
| 关键字 |
关键词:秦沈客运专线 钢轨铝热焊 焊接缺陷 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|